SABIC PBT VALOX™ 420SE0
VALOX™ 420SE0 resin
Polybutylene Terephthalate
SABIC Innovative Plastics
30% 玻璃纤维增强材料
产品说明：30% glass reinforced, UL94 V-0/5V rated. Numerous applications: edge trimmers, food mixer motor stator and commutator, cooling fan, connectors, bobbins, switches etc
物性信息：
| 基本信息 | |
| 黄卡编号 | E121562-101092083 E121562-101513781 |
| 填料/增强材料 | 玻璃纤维增强材料, 30% 填料按重量 |
| 用途 | 开关 连接器 |
| 加工方法 | 注射成型 |
| 多点数据 | Flexural DMA (ASTM D4065) Instrumented Impact (Energy) (ASTM D3763) Instrumented Impact (Load) (ASTM D3763) Shear DMA (ASTM D4065) Specific Heat vs. Temperature (ASTM D3417) Tensile Creep (ASTM D2990) Tensile Fatigue Tensile Stress vs. Strain (ASTM D638) Viscosity vs. Shear Rate (ASTM D3835) |
| 物理性能 | 额定值 | 单位制 | 测试方法 |
| 比重 | 1.63 | g/cm³ | ASTM D792, ISO 1183 |
| 特定体积 | 0.610 | cm³/g | ASTM D792 |
| 熔流率（熔体流动速率） (250°C/5.0 kg) | 42 | g/10 min | ASTM D1238 |
| 溶化体积流率（MVR） (250°C/5.0 kg) | 29.0 | cm³/10min | ISO 1133 |
| 收缩率 | 内部方法 | ||
| 流动 1 | 0.10 到 0.50 | % | 内部方法 |
| 流动 : 3.20 mm | 0.50 到 0.70 | % | 内部方法 |
| 横向流动 2 | 0.40 到 0.80 | % | 内部方法 |
| 横向流动 : 3.20 mm | 0.50 到 1.0 | % | 内部方法 |
| 吸水率 | ISO 62 | ||
| 饱和, 23°C | 0.090 | % | ISO 62 |
| 平衡, 23°C, 50% RH | 0.070 | % | ISO 62 |
| 室外适用性 | f2 | UL 746C |
| 硬度 | 额定值 | 单位制 | 测试方法 |
| 洛氏硬度 | |||
| R 级 | 119 | ASTM D785 | |
| R 计秤 | 119 | ISO 2039-2 | |
| 球压硬度 (H 358/30) | 118 | MPa | ISO 2039-1 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
| 拉伸模量 | |||
| -- 3 | 12000 | MPa | ASTM D638 |
| -- | 10000 | MPa | ISO 527-2/1 |
| 抗张强度 | |||
| 屈服 4 | 120 | MPa | ASTM D638 |
| 屈服 | 120 | MPa | ISO 527-2/5 |
| 断裂 5 | 120 | MPa | ASTM D638 |
| 断裂 | 120 | MPa | ISO 527-2/5 |
| 伸长率 | |||
| 屈服 6 | 2.0 | % | ASTM D638 |
| 屈服 | 1.9 | % | ISO 527-2/5 |
| 断裂 7 | 2.0 | % | ASTM D638 |
| 断裂 | 1.9 | % | ISO 527-2/5 |
| 弯曲模量 | |||
| 50.0 mm 跨距 8 | 9800 | MPa | ASTM D790 |
| -- 9 | 9500 | MPa | ISO 178 |
| 弯曲应力 | |||
| -- | 180 | MPa | ISO 178 |
| 断裂, 50.0 mm 跨距 10 | 186 | MPa | ASTM D790 |
| 泰伯耐磨性 (1000 Cycles, 1000 g, CS-17 转轮) | 22.0 | mg | 内部方法 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
| 简支梁缺口冲击强度 11 | ISO 179/1eA | ||
| -30°C | 6.0 | kJ/m² | ISO 179/1eA |
| 23°C | 7.0 | kJ/m² | ISO 179/1eA |
| 简支梁无缺口冲击强度 12 | ISO 179/1eU | ||
| -30°C | 50 | kJ/m² | ISO 179/1eU |
| 23°C | 50 | kJ/m² | ISO 179/1eU |
| 悬壁梁缺口冲击强度 | |||
| -30°C | 57 | J/m | ASTM D256 |
| 23°C | 60 | J/m | ASTM D256 |
| -30°C 13 | 6.0 | kJ/m² | ISO 180/1A |
| 23°C 14 | 7.0 | kJ/m² | ISO 180/1A |
| 无缺口悬臂梁冲击 | |||
| 23°C | 620 | J/m | ASTM D4812 |
| -30°C 15 | 45 | kJ/m² | ISO 180/1U |
| 23°C 16 | 45 | kJ/m² | ISO 180/1U |
| 装有测量仪表的落镖冲击 (23°C, Total Energy) | 5.00 | J | ASTM D3763 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
| 载荷下热变形温度 | |||
| 0.45 MPa, 未退火, 3.20 mm | 212 | °C | ASTM D648 |
| 0.45 MPa, 未退火, 100 mm 跨距 17 | 220 | °C | ISO 75-2/Be |
| 1.8 MPa, 未退火, 3.20 mm | 200 | °C | ASTM D648 |
| 1.8 MPa, 未退火, 100 mm 跨距 18 | 195 | °C | ISO 75-2/Ae |
| 1.8 MPa, 未退火, 64.0 mm 跨距 19 | 200 | °C | ISO 75-2/Af |
| 维卡软化温度 | |||
| -- | 200 | °C | ASTM D1525, ISO 306/B50, ISO 306/B120 20 |
| -- | 220 | °C | ISO 306/A50 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| 线形热膨胀系数 | |||
| 流动 : -40 到 40°C | 2.5E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| 流动 : 23 到 80°C | 2.5E-5 | cm/cm/°C | ISO 11359-2 |
| 横向 : -40 到 40°C | 8.9E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| 横向 : 23 到 80°C | 1.2E-4 | cm/cm/°C | ISO 11359-2 |
| 导热系数 | 0.25 | W/m/K | ISO 8302 |
| RTI Elec | 130 | °C | UL 746 |
| RTI Imp | 130 | °C | UL 746 |
| RTI | 140 | °C | UL 746 |
| 电气性能 | 额定值 | 单位制 | 测试方法 |
| 表面电阻率 | > 1.0E+15 | ohms | IEC 60093 |
| 体积电阻率 | > 1.0E+15 | ohms·cm | ASTM D257, IEC 60093 |
| 介电强度 | |||
| 1.60 mm, in Oil | 24 | kV/mm | ASTM D149 |
| 3.20 mm, in Air | 19 | kV/mm | ASTM D149 |
| 0.800 mm, 在油中 | 23 | kV/mm | IEC 60243-1 |
| 1.60 mm, 在油中 | 22 | kV/mm | IEC 60243-1 |
| 3.20 mm, 在油中 | 16 | kV/mm | IEC 60243-1 |
| 介电常数 | |||
| 100 Hz | 3.80 | ASTM D150, IEC 60250 | |
| 1 MHz | 3.70 | ASTM D150 | |
| 50 Hz | 3.30 | IEC 60250 | |
| 60 Hz | 3.30 | IEC 60250 | |
| 1 MHz | 3.30 | IEC 60250 | |
| 耗散因数 | |||
| 100 Hz | 2.0E-3 | ASTM D150, IEC 60250 | |
| 1 MHz | 0.020 | ASTM D150 | |
| 50 Hz | 1.0E-3 | IEC 60250 | |
| 60 Hz | 1.0E-3 | IEC 60250 | |
| 1 MHz | 0.010 | IEC 60250 | |
| 耐电弧性 21 | PLC 6 | ASTM D495 | |
| 相比耐漏电起痕指数(CTI) | PLC 3 | UL 746 | |
| 漏电起痕指数 | IEC 60112 | ||
| -- | 175 | V | IEC 60112 |
| 解决方案 B | 125 | V | IEC 60112 |
| 高电弧燃烧指数(HAI) | PLC 0 | UL 746 | |
| 高电压电弧起痕速率 (HVTR) | PLC 4 | UL 746 | |
| 热丝引燃 (HWI) | PLC 2 | UL 746 |
| 可燃性 | 额定值 | 单位制 | 测试方法 |
| UL 阻燃等级 | UL 94 | ||
| 0.400 mm | V-2 | UL 94 | |
| 0.710 mm | V-0 | UL 94 | |
| 2.00 mm | 5VA | UL 94 | |
| 灼热丝易燃指数 (1.00 mm) | 960 | °C | IEC 60695-2-12 |
| 极限氧指数 | 32 | % | ISO 4589-2 |
| 注射 | 额定值 | 单位制 | |
| 干燥温度 | 121 | °C | |
| 干燥时间 | 3.0 到 4.0 | hr | |
| 干燥时间，最大 | 12 | hr | |
| 建议的最大水分含量 | 0.020 | % | |
| 建议注射量 | 40 到 80 | % | |
| 料筒后部温度 | 243 到 266 | °C | |
| 料筒中部温度 | 249 到 271 | °C | |
| 料筒前部温度 | 254 到 277 | °C | |
| 射嘴温度 | 249 到 271 | °C | |
| 加工（熔体）温度 | 254 到 277 | °C | |
| 模具温度 | 65.6 到 87.8 | °C | |
| 背压 | 0.345 到 0.689 | MPa | |
| 螺杆转速 | 50 到 80 | rpm | |
| 排气孔深度 | 0.025 到 0.038 | mm |
| 备注 | |
| 1 . | Tensile Bar |
| 2 . | Tensile Bar |
| 3 . | 5.0 mm/min |
| 4 . | 类型 1, 5.0 mm/min |
| 5 . | 类型 1, 5.0 mm/min |
| 6 . | 类型 1, 5.0 mm/min |
| 7 . | 类型 1, 5.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 2.0 mm/min |
| 10 . | 1.3 mm/min |
| 11 . | 80*10*4 sp=62mm |
| 12 . | 80*10*4 sp=62mm |
| 13 . | 80*10*4 |
| 14 . | 80*10*4 |
| 15 . | 80*10*4 |
| 16 . | 80*10*4 |
| 17 . | 120*10*4 mm |
| 18 . | 120*10*4 mm |
| 19 . | 80*10*4 mm |
| 20 . | 标准 B (120°C/h), 载荷2 (50N) |
| 21 . | 钨电极 |